1450C Magnesia Refractory Bricks High Load Softening Temperature

1450C Magnesia Refractory Bricks High Load Softening Temperature

large.img.alt
small.img.alt

Large Image :  1450C Magnesia Refractory Bricks High Load Softening Temperature

Product Details:
Place of Origin: Henan Xinmi
Brand Name: Kaier
Certification: ISO9001
Model Number: HYM-92
Payment & Shipping Terms:
Minimum Order Quantity: 10Ton
Price: Negotiated
Packaging Details: Pallet Size :92x92x100cm ,Cardboard&Corner Protection,Waterproof Film
Delivery Time: 5days after got deposit
Payment Terms: L/C, T/T,
Supply Ability: 2000Ton Per Month
Detailed Product Description
Type: Magnesia Refractory Bricks Mgo Content: 88% - 97%
Al2o3 Content: Around 5% Sinterd Temperature: 1450℃
Feature: High Load Softening Temperature Apparent Porosity: ≤18
Bulk Density: 2.7-3.0 Working Temperature: 1400℃
High Light:

1450C Magnesia Refractory Bricks

,

97% MGo Magnesia Refractory Bricks

,

magnesite refractory bricks 88% MGo

1450C Magnesia Refractory Bricks High Load Softening Temperature​

 

The Magnesia Refractory Bricks with MgO 95% or more in content take the secondary-burning dead burned magnesia or electrofused magnesia as the raw material and bured under the condition of ultra high temperature. They have the features of highly directly bonded and corrosion-resistance and widely used in various kinds of high temperature kilns and furnaces.

 

Magnesia Refractory Bricks Features

1. High refractoriness, usually the refractoriness is above 2000°C.
2. Refractoriness under load about 1500-1550°C because of poor high-temperature intensity.
3. Strong ability to resist basic (alkaline) slag, can not contact with acid refractory material.

 

Magnesia Refractory BricksTechnical Data

 

Item MZ-97 MZ-95 MZ-93 MZ-91
MgO % ≥97 ≥95 ≥93 ≥91
SiO2 % ≤1.0 ≤2.0 ≤3.5 -
CaO % - ≤2.0 ≤2.0 ≤3.0
Apparent porosity/% ≤16 ≤16 ≤18 ≤18
Cold crushing strength/ Mpa ≥60 ≥60 ≥60 ≥60
Refractoriness under load, 0.2MPa, °C ≥1700 ≥1650 ≥1620 ≥1560
Reheating Linear Change(1650 °C,2h) /% 0~-0.2 0~-0.3 0~-0.4 0~-0.4


Applications

1. Iron Steel Industry
steelmaking furnace lining, ferroalloy furnace, metal mixer furnace lining, converter lining, arc furnace wall and furnace bottom, soaking furnace, heating furnace bottom

2. Non-ferrous metallurgical industry
copper,nickel,lead,zinc,tin smelting furnace lining, refined copper reverberatory furnace,ore electric furnace lining

3. Glass Industry
glass furnace regenerator checker

4. Building Material Industry
lime kiln,cement kiln


Shapes & Sizes

 

Straight Split Arch Wedge Tile Other Shape
L×W×H(mm) L×W×H (mm) L×W×H/h(mm) L×W×H/h (mm) L×W×H (mm) Key brick,
230×114×65 230×114×25 230×114×65/45 230×114×65/45 230×230×38 Skew brick,
230×114×75 230×114×32 230×114×65/55 230×114×65/55 230×230×50 Soap,
  230×114×37 230×114×75/45 220×114×75/45 230×230×65 Checker,
  230×114×50 230×114×75/55 220×114×75/55 230×230×75 Neck,
    230×114×75/65 220×114×75/65   Taper,

We also can make brick according to customers’ drawing and requirements.

 

1450C Magnesia Refractory Bricks High Load Softening Temperature 0

1450C Magnesia Refractory Bricks High Load Softening Temperature 1

 

Contact Details
ZhengZhou Kaier Kiln Refractory Co.,Ltd

Contact Person: Mika

Tel: 86-15981951014

Send your inquiry directly to us (0 / 3000)

Contact Us Quickly