|Al2o3:||65%-75%||Raw Materials:||Calcined Bauxite|
|Application:||Industrial Furnaces, Metallurgy||Color:||Light Yellow|
|Size:||As Request||Bulk Density:||2.3-2.7 G/cm3|
alumina fire brick,
fire resistant bricks
65% - 75% Al2o3 Alumina Refractory Bricks Good Resistance To Abrasion
High-aluminum bricks are mainly used for masonry blast furnaces, hot blast stoves, electric furnace tops, blast furnaces, reverberatory furnaces, and rotary kiln linings. In addition, high-aluminum bricks are also widely used as open-hearth regenerative lattice bricks, plugs for gating systems, and shingles.
The first-grade high-alumina brick (the aluminum content is not less than 75% refractory brick) is formed by pressing and calcining a high-quality raw material such as high-quality bauxite and alumina. The high-aluminum brick has a refractoriness of over 1790 °C. The load softening temperature is above 1510 °C, the thermal shock stability is good, and the slag resistance is good. It is mainly used for ladle furnace, masonry blast furnace (furnace, belly), hot blast stove (upper), electric furnace cover (top) Blast furnace, reverberatory furnace, rotary kiln lining etc...
1. Good resistance to abrasion and corrosion,
2. Good volume stability at high temperature,
3. Chemical attack to provide long service life,
4. Easy operation and installation,
5. Broad usage or applications and low price.
|Item&Grade||Fire Clay Brick||High Alumina Brick|
|Refractoriness Under Load,0.2Mpa ℃ (≥)||1250||1300||1360||1420||1450||1480||1530||1600|
|Apparent Porosity (%)||22-26||20-24||20-22||18-20||20-23||20-23||20-22||18-20|
|Bulk Density (g/cm3)||1.9-2.0||1.95-2.1||2.1-2.2||2.15-2.2||2.25-2.4||2.3-2.5||2.4-2.6||2.5-2.7|
|Cold Crushing Strengh, Mpa (≥)||20||25||30||40||45||50||60||70|