Product Details:
Payment & Shipping Terms:
|
| Product Name: | Fire Clay Brick | Raw Materials: | Bauxite |
|---|---|---|---|
| Al2o3 Content (%): | 45%-55% | Application: | Industrial Furnace |
| Size: | Standard Size :230x114x65mm | Color: | Red Fire |
| Bulk Density: | 2.1-2.25g/cm3 | Shape: | Brick |
| Refractoriness: | Common (1580°< Refractoriness< 1770°) | Type: | 3 Level Of High Alumina Brick |
| High Light: | refractory clay bricks,fireplace refractory brick |
||
Compact Design Fire Clay Bricks SK-36 SK-38 Low Thermal Conductivity
Product Description
Fireclay brick is made from clinker clay by mixing, forming, drying, sintering and matching characterized by good resistance to corrosion and abrasion, good thermal shock resistance, good spelling resistance, high mechanical strength, good volume stability under high temperature.
Features
1. Low bulk density, low thermal conductivity, good thermal insulation performance.
2. Refractory category allow direct contact of fire, suitable ofr various atmosphere
3. Good integrity with furnace lining, long service life, easy operation, could be shaped freely
4. Product specification: standard form, normal standard, shaped and special shaped bricks.
5. Can be used in various kilns because of its cheapness and general tray package. Among all of the refractory materials, it is the most widely used.
Application:
1) Cement and other building materials industry kiln back insulation;
2) Petrochemical, metallurgical, ceramics, glass industry, the furnace lining insulation;
3) Heat treatment furnace backlash insulation;
4) Non-ferrous metal industry back insulation;
5) High temperature reaction, heating equipment back insulation insulation
Specification
| Item | SK-30 | SK-32 | SK-34 | SK-36 | SK-38 |
| AL2O3% (min) | 30-35% | 35-38% | 38-42% | 50-55% | 60-65% |
| Fe2O3% (max) | 3 | 3 | 2.8 | 2.5 | 2.3 |
| Refractoriness | ≥1670°C | ≥1690°C | ≥1710°C | ≥1750°C | ≥1770°C |
| Refractoriness under load, 0.2MPa, (°C) | ≥1270 | ≥1350 | ≥1350 | ≥1430 | ≥1450 |
| Apparent porosity (%) | 20-24 | 20-24 | 19-23 | 18-22 | 18-22 |
| Bulk density (g/cm³) | 2.00-2.05 | 2.05-2.1 | 2.1-2.15 | 2.15-2.25 | 2.25-2.35 |
| Cold crushing strength (MPa) | ≥25 | ≥30 | ≥35 | ≥45 | ≥50 |
| Thermal expansion at 1000°C (%) | ≤0.6 | ≤0.55 | ≤0.55 | ≤0.4 | ≤0.4 |
Detail Show