ZhengZhou Kaier Kiln Refractory Co.，Ltd
ZhengZhou Kaier Kiln Refractory Co.，Ltd
Professional Refractory Bricks Supplier |
|
Product Details:
Payment & Shipping Terms:
|
| Main Ingredient: | Sinterd Fused Magnesite Powder | Mgo Content: | 88% - 97% |
|---|---|---|---|
| Al2o3 Content: | Around 5% | Sinterd Temperature: | 1450℃ |
| Color: | Black Color | Apparent Porosity: | ≤18 |
| Bulk Density: | 2.7-3.0 | Working Temperature: | 1400℃ |
| High Light: | kiln refractory bricks,heat proof bricks |
||
High Refractoriness Magnesite Refractory Bricks 1450℃ Sinterd Temperature
Feature of HengYu Magnesite Refractory Bricks
1. High refractoriness, usually the refractoriness is above 2000°C.
2. Refractoriness under load about 1500-1550°C because of poor high-temperature intensity.
3. Strong ability to resist basic (alkaline) slag, can not contact with acid refractory material.
4. Poor Thermal shock resistance, so keep the temperature of furnace stabilized.
5. Poor Volume stability at high temperature, must set aside appropriate expansion joint when laying brick.
6. Strong ability of thermal conductivity, sometime need insulating material.
7. Hydrability, keep product away from moisture during storage.
Magnesite Refractory Bricks Description
1.The products are fused magnesia as main raw material, after a reasonable size distribution, high pressure forming, high-temperature sintering. The product has strong resistance to slag corrosion ability and high temperature dimensional stability. Mainly used in glass furnace regenerator, the upper part.
2.The regular magnesia bricks are made from dense dead burned magnesia that makes the bricks in good refractoriness, corrosion-resistance, and widely used in checker chamber of glass tank, lime kiln, non-ferrous metallurgical furnaces, open heart furnace, iron mixer and EAF of steel-making, and also ferro-alloy furnace, etc.
Magnesite Refractory Bricks Technical Data
| Item | MZ-97 | MZ-95 | MZ-93 | MZ-91 |
| MgO % | ≥97 | ≥95 | ≥93 | ≥91 |
| SiO2 % | ≤1.0 | ≤2.0 | ≤3.5 | - |
| CaO % | - | ≤2.0 | ≤2.0 | ≤3.0 |
| Apparent porosity/% | ≤16 | ≤16 | ≤18 | ≤18 |
| Cold crushing strength/ Mpa | ≥60 | ≥60 | ≥60 | ≥60 |
| Refractoriness under load, 0.2MPa, °C | ≥1700 | ≥1650 | ≥1620 | ≥1560 |
| Reheating Linear Change(1650 °C,2h) /% | 0~-0.2 | 0~-0.3 | 0~-0.4 | 0~-0.4 |
Applications
1. Iron Steel Industry
steelmaking furnace lining, ferroalloy furnace, metal mixer furnace lining, converter lining, arc furnace wall and furnace bottom, soaking furnace, heating furnace bottom
2. Non-ferrous metallurgical industry
copper,nickel,lead,zinc,tin smelting furnace lining, refined copper reverberatory furnace,ore electric furnace lining
3. Glass Industry
glass furnace regenerator checker
4. Building Material Industry
lime kiln,cement kiln
5. Refractory Material Industry
High temperature calcination kiln,shaft kiln and tunnel kiln
Shapes & Sizes
| Straight | Split | Arch | Wedge | Tile | Other Shape |
| L×W×H(mm) | L×W×H (mm) | L×W×H/h(mm) | L×W×H/h (mm) | L×W×H (mm) | Key brick, |
| 230×114×65 | 230×114×25 | 230×114×65/45 | 230×114×65/45 | 230×230×38 | Skew brick, |
| 230×114×75 | 230×114×32 | 230×114×65/55 | 230×114×65/55 | 230×230×50 | Soap, |
| 230×114×37 | 230×114×75/45 | 220×114×75/45 | 230×230×65 | Checker, | |
| 230×114×50 | 230×114×75/55 | 220×114×75/55 | 230×230×75 | Neck, | |
| 230×114×75/65 | 220×114×75/65 | Taper, | |||
|
We also can make brick according to customers’ drawing and requirements. |
|||||